Metallurgical specifications of Sheets and Strips of Aluminum 2014

General Characteristics
The 2014 alloy is one of the strongest heat-treatable alloys for screw machine applications. This alloy, commonly found in forging applications, offers good machinability and high strength. Corrosion resistance is only fair; however, weldability is good with arc and resistance methods. In many applications this alloy may be substituted with 2024.
Typical Chemical Composition

Others

Weight % Si Fe Cu Mn Mg Cr Zn Ti Each Total Aluminium

Minimum 0.5 — 3.9 0.4 0.2 — — — — — Remainder

Maximum 1.2 0.7 5.0 1.2 0.8 0.1 0.25 0.15 0.05 0.15

	Others
Minimum	0.5	—	3.9	0.4	0.2	—	—	—	—	—	Remainder
Maximum	1.2	0.7	5.0	1.2	0.8	0.1	0.25	0.15	0.05	0.15

Characteristics		English	Metric
Nominal density (68°F/20°C)		0.101 lbs/in³	2.80 mg/m³
Melting range		945°F-1180°F	507°C-638°C
Specific heat (212 °F/100°C)		0.206 BTU/lb – °F	864 J/KG- °K
Coefficient of thermal expansion	Linear 68°F – 212°F 20°C – 100°C	12.5 micro in/in- °F	22.5 micro in/in- °K
Coefficient of thermal expansion	Volumetric 68 ºF / 20 ºC	3.62 x 10^-5 in.³/in.³ – ºF	65.1 x 10-6 m³/m³ – ºK
Thermal conductivity (68°F/20°C)	O Temper	111 BTU/ft- hr – °F	192 W/m – °K
	T4, T451	77.4 BTU/ft- hr – °F	134 W/m – °K
	T6, T651	89.5 BTU/ft- hr – °F	155 W/m – °K
Electrical conductivity (68°F/20°C)	Equal volume	O Temper	50% IACS
		T4, T451	34% IACS
		T6, T651	40% IACS
	Equal Weight	O Temper	159% IACS
		T4, T451	108% IACS
		T6, T651	127% IACS

Temper	Tensile					Hardness	Shear		Fatigue		Modulus
	Ultimate Thickness 0.5- 12.7 mm 0.02-0.5 In.		Yield Thickness 0.5-12.7 mm 0.02-0.5 In.		Elongation/ 4D	Brinell 500 kg 10 mm	Ultimate shearing strength		Endurance limit-R.R.Moore type		Modulus of elasticity
	KSI	MPa	KSI	MPa	Thickness 0.5-12.7 mm 0.02-0.5 In.		KSI	MPa	KSI	MPa	KSIx10³	Gpa
O	31.9	220	16	110	16	45	18	125	13	90	10.6	73.1
T-4	58	400	34.1	235	14	105	38	260	20	140	10.6	73.1
T-6	63.8-66	440-445	57.3	395	4-7	135	42	290	18	125	10.6	73.1

Aluminum Alloy 2014 Sales:+972 4 618 2000

General Characteristics
The 2014 alloy is one of the strongest heat-treatable alloys for screw machine applications. This alloy, commonly found in forging applications, offers good machinability and high strength. Corrosion resistance is only fair; however, weldability is good with arc and resistance methods. In many applications this alloy may be substituted with 2024.
Typical Chemical Composition

Others

Weight % Si Fe Cu Mn Mg Cr Zn Ti Each Total Aluminium

Minimum 0.5 — 3.9 0.4 0.2 — — — — — Remainder

Maximum 1.2 0.7 5.0 1.2 0.8 0.1 0.25 0.15 0.05 0.15

	Others
Minimum	0.5	—	3.9	0.4	0.2	—	—	—	—	—	Remainder
Maximum	1.2	0.7	5.0	1.2	0.8	0.1	0.25	0.15	0.05	0.15

Characteristics		English	Metric
Nominal density (68°F/20°C)		0.101 lbs/in³	2.80 mg/m³
Melting range		945°F-1180°F	507°C-638°C
Specific heat (212 °F/100°C)		0.206 BTU/lb – °F	864 J/KG- °K
Coefficient of thermal expansion	Linear 68°F – 212°F 20°C – 100°C	12.5 micro in/in- °F	22.5 micro in/in- °K
Coefficient of thermal expansion	Volumetric 68 ºF / 20 ºC	3.62 x 10^-5 in.³/in.³ – ºF	65.1 x 10-6 m³/m³ – ºK
Thermal conductivity (68°F/20°C)	O Temper	111 BTU/ft- hr – °F	192 W/m – °K
	T4, T451	77.4 BTU/ft- hr – °F	134 W/m – °K
	T6, T651	89.5 BTU/ft- hr – °F	155 W/m – °K
Electrical conductivity (68°F/20°C)	Equal volume	O Temper	50% IACS
		T4, T451	34% IACS
		T6, T651	40% IACS
	Equal Weight	O Temper	159% IACS
		T4, T451	108% IACS
		T6, T651	127% IACS

Temper	Tensile					Hardness	Shear		Fatigue		Modulus
	Ultimate Thickness 0.5- 12.7 mm 0.02-0.5 In.		Yield Thickness 0.5-12.7 mm 0.02-0.5 In.		Elongation/ 4D	Brinell 500 kg 10 mm	Ultimate shearing strength		Endurance limit-R.R.Moore type		Modulus of elasticity
	KSI	MPa	KSI	MPa	Thickness 0.5-12.7 mm 0.02-0.5 In.		KSI	MPa	KSI	MPa	KSIx10³	Gpa
O	31.9	220	16	110	16	45	18	125	13	90	10.6	73.1
T-4	58	400	34.1	235	14	105	38	260	20	140	10.6	73.1
T-6	63.8-66	440-445	57.3	395	4-7	135	42	290	18	125	10.6	73.1

Aluminum Alloy 2014